RT Journal Article
T1 Critical temperature depression and persistent photoconductivity in ion irradiated YBa2Cu3O7-x films and YBa2Cu3O7-x/PrBa2Cu3O7 superlattices
A1 Lucía Mulas, María Luisa
A1 Sánchez Quesada, Francisco
A1 Santamaría Sánchez-Barriga, Jacobo
A1 Sefrioui, Zouhair
A1 Arias Serna, Diego
A1 Loos, G.
A1 Navacerrada, M.A.
AB We have studied the effect of He+ irradiation with doses in the range 10(12)-2x10(15) cm(-2) on two high-temperature superconducting structures: YBa2Cu3O7-x (YBCO) films and YBa2Cu3O7-x/PrBa2Cu3O7 (YBCO/PBCO) superlattices. In particular we have focused on superlattices [YBCON/PBCOM](1000 Angstrom) with N=1, 8 unit cells of YBCO, and M=5 unit cells of PBCO, with a total thickness of 1000 Angstrom. The analysis is presented in terms of depression of the critical temperature (T-c) and modification of the crystalline structure using X ray refinement technique. Single films show a systematic increase in the c-lattice parameter upon irradiation, which is not observed in thin one unit cell YBCO layers in superlattice structures. However, T-c depression resulting from irradiation is deeper in superlattices. These results are explained considering the strained nature of the as-grown [YBCON/PBCO5](1000 Angstrom) superlattices with low values of N. Both structures show persistent photoconductivity, indicating that defects are related to oxygen displacements in the Cu-O chains.
PB Amer Inst Physics
SN 0003-6951
YR 2000
FD 2000-05-29
LK https://hdl.handle.net/20.500.14352/59333
UL https://hdl.handle.net/20.500.14352/59333
LA eng
NO © American Institute of Physics. G.L. thanks the SAB1995-0685 to Ministerio de Educación y Cultura. Financial support from CICYT grant MAT970675/96-7054 is also acknowledged. Implantation experiments have been carried out at the CAI of Universidad Complutense.
NO Ministerio de Educación y Cultura
NO CICYT
DS Docta Complutense
RD 5 abr 2025