%T Structural, magnetic and luminescent characteristics of Pr3+-doped ZrO2 powders synthesized by a sol–gel method
%D 2009
%@ 0022-3727
%U https://hdl.handle.net/20.500.14352/95166
%X The structural, magnetic and luminescence properties of praseodymium-doped zirconia powders of compositions Pr0.03Zr0.97O2 and Pr0.05Zr0.95O2 synthesized by a sol–gel process have been investigated. X-ray diffraction patterns indicate that these materials crystallize in a tetragonal fluorite-type structure. Scanning electron microscopy shows that the powders exhibit an agglomerated microcrystalline structure and the grain size may be in the order of 5–20μm. The study of the magnetic properties of these doped metal oxides indicates a Curie–Weiss behaviour in the temperature range (100–300)K that allow us to estimate an effective magnetic moment of 3.51μB, which indicates the presence of Pr3+ in the grown samples. Cathodoluminescence spectra recorded at temperatures between 85 and 295K show emission peaks that can be attributed to transitions between different states within the 4f2 configuration of Pr3+ ions incorporated in the zirconia crystal lattice. Thermoluminescence measured at temperatures ranging from 373 to 773K and at 550 nm wavelength show an intense and broad peak around 653K for the Pr-doped zirconia which is not observed in the undoped material.
%~