Docta Complutense
author
Bisero, D.
author
Fin, S.
author
Ranchal Sánchez, Rocío
2023-06-17T22:05:55Z
2023-06-17T22:05:55Z
2017-04-30
0040-6090
10.1016/j.tsf.2017.03.033
https://hdl.handle.net/20.500.14352/18059
http://dx.doi.org/10.1016/j.tsf.2017.03.033
http://www.sciencedirect.com
The interest in Tb-Fe-Ga alloys, prepared by techniques compatible with technological processes, has been increasing in the last years, due to their high magnetostriction combined with their potential application in spintronic devices. In this letter, we report the domain configurations of a Tb10Fe76Ga14 thin film grown by co sputtering deposition. The film exhibits a weak perpendicular magnetic anisotropy (PMA) and the presence of discontinuous stripe domains. The application of an external field in the film plane, perpendicular to the stripe direction, induces the rotation of the stripes and the alignment of their axis with the field. This property of the material has been observed in the range of applied fields 0-70 mT, above which PMA disappears and stripe annihilation occurs.
eng
Rotation of stripe domains in a sputter deposited Tb-Fe-Ga thin film
journal article
URL
https://docta.ucm.es/bitstreams/d6382d67-4ed3-48e1-915e-576a9aade6c1/download
File
MD5
0096ac46e5f86d6e0293ce45bf9dfa5b
186788
application/pdf
Ranchal 04 postprint+EMB 01_05_2019.pdf
URL
https://docta.ucm.es/bitstreams/7fc4f3e8-c640-4ba2-959a-adbc00e9f9a5/download
File
MD5
718979bdb3291f142dd5eb5ee27924b9
25204
text/plain
Ranchal 04 postprint+EMB 01_05_2019.pdf.txt