Purpose: Using a simulated perfusion system, the intent was to determine: 1) the sealing ability of eight
restorative materials (five composite resins and three compomers) used together with their corresponding dentin bonding systems, 2) their tensile bond strength, and 3) the correlation (if any) between both parameters.
Materials and Methods: Permeability in crown segments from sound human third molars (n = 140) subjected to simulated perfusion (32 cm of distilled water) was measured before and after restoring with each material, and the percentage of decrease in permeability ((PPD) was recorded. Specimens were tater subjected to tensile tests to determine the tensile bond strength (TBS) of the interface. Finally, parameters were analyzed for correlation.
Results: For the eight adhesive systems, the percentage of reduction in permeability was relatively hlgh [mean in %, (SD)]: F2000 93.6 (5.7),S B188.6 (11.31,S SC 86.0 (5.7), PB20 81.1 (15.9)C,O M 77.5 (10.8), OPTS 75.3 (20.6)D,Y R 73.7 (12.7)S,S PR 65.5 (19.8)T.B S values were relatively low [mean (SD)], in MPa: F2000 1.8 (0.71, SB1 4.9 (1.4)S,S C 2.6 (1.4), PB20 4.3 (1.21,C OM 2.4 {1.1),O PTS 4.5 (1.7)D,Y R L6 (0.6), SSPR.4.2 (1.5). We could not demonstrate any statistically significant correlation between both parameters for these results (maximum significance [F20001: r = 0.39, p = 0.206).
Conclusion: No material completely ceased to filtrate through the interface. The low TBS values were probably due to the large size of adhesive areas. No significant correlation was found between PPD and TBS
for the materials tested. There was a statistically significant relationship (r2 = 0.063, p = 0.018) between
TBS and TEA (total bonded area), described by the equation TBS = 5.9 - 0.03'TBA.
spa
Analysis of sealing vs tensile bond strength of eight adheisve restorative material systems
journal article
URL
https://docta.ucm.es/bitstreams/591c7440-ce8c-4204-bb7b-8a3b711c4ea1/download
File
MD5
ab10f11d16a2e50e3426840ef2868f71
2778480
application/pdf
Analysis_of_sealing_vs_tensile_bond_strength_of_eight_adheisve_restorative_material_systems.pdf
URL
https://docta.ucm.es/bitstreams/55bf8e67-b486-4b32-ae6f-7acf3905767c/download
File
MD5
6cccda74febad7705949cb89ee2669dd
22
text/plain
Analysis_of_sealing_vs_tensile_bond_strength_of_eight_adheisve_restorative_material_systems.pdf.txt