Transition from AFM spin canting to spin glass-AFM exchange as particle size decreases in LaFeO_3 Alshalawi, Dhoha Alonso, Jose Maria Landa-Canovas, Angel R. Presa Muñoz De Toro, Patricia Marcela De La In this work, we have studied structural and magnetic properties of LaFeO_3 as a function of the particle size d, from bulk (d >> 1 µm) to nanoscale (d ≈ 30 nm). A large number of twins were observed for large particles that disappear for small particle sizes. This could be related to the softening of the FeO_6 distortion as particle size decreases. It was observed that the bulk sample showed spin canting that disappeared for d ~ 125 nm and can be associated with the smoothening of the orthorhombic distortion. On the other hand, for d < 60 nm, the surface/volume ratio became high and, despite the high crystallinity of the nanoparticle, a notable exchange effect bias appeared, originated by two magnetic interactions: spin glass and antiferromagnetism. This exchange bias interaction was originated by the formation of a "magnetic core-shell": the broken bonds at the surface atoms give place to a spin glass behavior, whereas the inner atoms maintain the antiferromagnetic G-type order. The LaFeO_3 bulk material was synthesized by the ceramic method, whereas the LaFeO_3 nanoparticles were synthesized by the sol-gel method; the particle size was varied by annealing the samples at different temperatures. The physical properties of the materials have been investigated by XRD, HRTEM, TGA, and AC and DC magnetometry. 2023-07-26T14:36:04Z 2023-07-26T14:36:04Z 2023-07-26T14:36:04Z 2023-05-17 journal article https://hdl.handle.net/20.500.14352/87342 XXXX-XXXX 10.3390/nano13101657 2079-4991 eng info:eu-repo/grantAgreement/AEI/Plan Estatal de Investigación Científica y Técnica y de Innovación 2021-2023/PID2021-123112OB-C21/ES/MATERIALES MAGNETICOS NANO Y MICROESTRUCTURADOS INTEGRADOS EN MINIATURIZADOS E INTELIGENTES SISTEMAS ANALITICOS PARA DETECTAR ENFERMEDADES MEDIANTE EL ALIENTO/ Alshalawi, D.; Alonso, J.M.; Landa-Cánovas, A.R.; de la Presa, P. Transition from AFM Spin Canting to Spin Glass–AFM Exchange as Particle Size Decreases in LaFeO3. Nanomaterials 2023, 13, 1657. https://doi.org/10.3390/nano13101657 http://creativecommons.org/licenses/by/4.0/ open access Attribution 4.0 International MDPI