Rodriguez Fernandez, BeatrizDolado, JaimeLópez Sánchez, JesúsHidalgo Alcalde, PedroMéndez Martín, Bianchi2023-06-222023-06-222023-032079-499110.3390/nano13050884https://hdl.handle.net/20.500.14352/73150© 2023 by the authors. Licensee MDPI, This work was supported by MICINN projects (RTI2018-097195-B-I00, PIE 2021-60-E-030, PIE 2010-6-OE-013 and PID2021-122562NB-I00). B.R. acknowledges financial support from MICINN (contract No. PRE2019-088162).Polymorphous WO_(3) micro- and nanostructures have been synthesized by the controlled Joule heating of tungsten wires under ambient conditions in a few seconds. The growth on the wire surface is assisted by the electromigration process and it is further enhanced by the application of an external electric field through a pair of biased parallel copper plates. In this case, a high amount of WO_(3) material is also deposited on the copper electrodes, consisting of a few cm^(2) area. The temperature measurements of the W wire agrees with the values calculated by a finite element model, which has allowed us to establish the threshold density current to trigger the WO_(3) growth. The structural characterization of the produced microstructures accounts for the gamma-WO_(3) (monoclinic I), which is the common stable phase at room temperature, along with low temperature phases, known as delta-WO_(3) (triclinic) on structures formed on the wire surface and e-WO_(3) (monoclinic II) on material deposited on external electrodes. These phases allow for a high oxygen vacancies concentration, which is interesting in photocatalysis and sensing applications. The results could help to design experiments to produce oxide nanomaterials from other metal wires by this resistive heating method with scaling-up potential.engAtribución 3.0 Españajournal articlehttp://dx.doi.org/10.3390/nano13050884https://www.mdpi.com/open access538.9TungstenNanowiresOxidesRamanxXpsTungsten trioxidePolymorphismJoule heatingElectromigrationFísica de materialesFísica del estado sólido2211 Física del Estado Sólido