Gutiérrez Martín, DanielHernando González, MaríaParras Vázquez, Marina MartaTorres Pardo, María De La AlmudenaFernández Díaz , Mª TeresaSavvin, SRodrigues, JoaoGonzález Calbet , Jose MªSilva Jr , RomualdoMartínez, Jose LuisVarela Losada, María Áurea2025-01-302025-01-302025-01-27Gutiérrez-Martín, D., et al. «Unveiling the Magnetic Structure of BaFeO3-y: Shedding Light on the Elusive Magnetic Behavior». Journal of Alloys and Compounds, vol. 1010, enero de 2025, p. 177081. DOI.org (Crossref), https://doi.org/10.1016/j.jallcom.2024.177081.10.1016/j.jallcom.2024.177081https://hdl.handle.net/20.500.14352/117283This work provides a comprehensive examination of the structural and magnetic properties of 6H-BaFeO2.96 over a wide temperature range (10 K < T < 300 K) using neutron and synchrotron X-ray diffraction. Additionally, the local oxidation state of iron is examined using electron energy loss spectroscopy. No structural changes that could indicate a charge-order transition are observed in spite of a reported possible charge disproportionation of Fe4+ into Fe(4+δ)+ and Fe(4-δ)+ phenomenon at low temperature. According to the magnetic characterization, BaFeO2.96 orders antiferromagnetically at TN=156 K. The application of external magnetic fields strongly influences the magnetic behavior; the transition temperature shifts to lower values with the applied magnetic field and the long-range magnetic order melts with an applied field of 14 T. The magnetocaloric effect clearly shows at TN a change from negative to positive magnetic entropy. The Rietveld refinement of the neutron powder diffraction data collected at 10 K, gives a magnetic ordering with propagation vector [0, 0, ½] and three magnetically distinct sites for the Fe atoms. This magnetic structure consists of ferromagnetic Fe-sheets perpendicular to the c-axis with the magnetic moments along the [110] direction coupled both ferromagnetic and antiferromagnetically along the c-axis. The magnetic moment values of the three Fe ions are very differentevidencing a delicate equilibrium of competing magnetic interactions.engAttribution-NonCommercial-NoDerivatives 4.0 Internationalhttp://creativecommons.org/licenses/by-nc-nd/4.0/journal articlehttps://doi.org/10.1016/j.jallcom.2024.177081open access546Structural study at low temperature6H-BaFeO2.96Local oxidation state of ironMagnetic propertiesMagnetic structureQuímica2303 Química Inorgánica